- Graphene coated aluminum foil for supercapacitor/power battery
- Cathode foil for Aluminum electrolytic capacitors
- Etching collector for supercapacitor
- Polymer carbon foil -Solid state capacitors
Etching collector for supercapacitor
超級電容用蝕刻集流體
(Etching collector for supercapacitor)
|
A1 layer |
|
Etching layer |
Etching current collector has alveolate structure on the surface to be filled by active substances. This current collector can effectively reduce the resistance caused by bad covering, and reduce heating generation of the super capacitor during large current charge and discharge, Improve the current charge and discharge capacity and heat-sinking capability.
|
Product Name |
Aluminum content |
Specific volume |
Thickness |
Tensile strength |
Bending |
Application Fields |
|
% |
(uf/cm2) |
(um) |
(kg/cm) |
(次) |
||
|
20SC01 |
≥ 99.7 |
20 |
20 ±2 |
≥ 2.5 |
≥ 60 |
EDLC |
|
22SC01 |
20 |
22 ± 2 |
≥ 2.5 |
≥ 60 |
||
|
30SC01 |
50 |
30 ± 3 |
≥ 3.0 |
≥70 |
||
|
40SC01 |
80 |
40 ± 4 |
≥ 3.0 |
≥ 80 |
||
|
Standard Capacitance ≥ -10% |
Foil Hardness: HARD |
|||||
|
Product Name |
Aluminum content |
Specific volume |
Thickness |
Tensile strength |
Bending |
Application Fields |
|
% |
(uf/cm2) |
(um) |
(kg/cm) |
(次) |
|
|
|
SCB205 |
≥ 99.6 |
20 |
22 ± 2 |
≥ 2.5 |
≥ 70 |
EDLC
Lithium-Ion
Polymer
Coating
|
|
SCB305 |
50 |
30 ± 3 |
≥ 3.0 |
≥ 90 |
||
|
SCB410 |
100 |
40 ± 4 |
≥ 3.0 |
≥ 100 |
||
|
LC200 |
≥ 99.4 |
0 |
22 ± 2 |
≥ 2.5 |
≥ 70 |
|
|
LC300 |
0 |
30 ± 3 |
≥ 3.0 |
≥ 90 |
||
|
LC400 |
0 |
40 ± 4 |
≥ 3.0 |
≥ 100 |
||
|
Standard Capacitance ≥ -10% |
Foil Hardness: HARD |
|||||